模压的制品 表面 有气泡 怎么办

玫70

<>我们用SMC  压制汽车面罩 但是表面总是有气泡，哪位高手 帮我分析一下原因</P>
<>先谢谢了</P>

sand

<>又是很trouble的问题！！！</P>
<>可能产生的原因如下：</P>
<>一、材质：</P>
<>1）Insufficient glass wet out with resin (dry glass)
玻璃纤维未能浸润</P>
<>2）Foreign objects/contamination (film, flash, etc.) in or on the charge
有杂质</P>
<>3）Wrinkles/pockets in discontinuous surface of SMC charge pattern
SMC表面不平整</P>
<>二、生产工艺：</P>
<>1）Adding small SMC pieces to charge pattern which trap air
小块的SMC补片内裹气（布料不良）</P>
<>2）Insufficient pressure on SMC during cure cycle
固化时压力不足</P>
<>3）Oven temperature heat-up rate too fast, especially in combination with a high moisture content part
烘箱加热太快，特别是含水率偏高时</P>
<P>4）Improper charge patter (too large, rolled or folded)
充填不良</P>
<P>5）Vacuum too low; improper vacuum cycle
排气动作不当</P>
<P>6）Low cure time (under cure)
固化时间太短（未完全固化）</P>
<P>7）Press closure speed to fast (air trapped in laminate)
合模速度太快</P>
<P>三、模具：</P>
<P>1）Mold shear edge is too tight (not allowing air to bleed out)
模具间隙太小（无法排气）</P>
<P>2）Tool Deflection
加工尺寸偏差</P>

[此贴子已经被作者于2006-4-6 12:07:03编辑过]

玫70

<>翻译成中文 如何 谢谢。</P>

sand

<>简单翻译了一下，凑或着看看吧。建议还是看英文，翻译水平有限，有些意思中文很难表达。</P>

玫70

谢谢

丹晨子

在片材没有熟化好的时候,既是粘度不大时,也会造成产品表面有气泡和气孔产生.

letgo508

<>在片材暂时不好改的情况下,调整模压工艺,主要在加料方式上调整看看.另外你的抽真空不?</P>

玫70

<B></B>
<>在片材暂时不好改的情况下,调整模压工艺,主要在加料方式上调整看看.另外你的抽真空不?</P><>怎么抽真空啊 没有接触过啊</P>

letgo508

<>在模具上下摸咬死后开始抽真空,大概20mm左右的位置,这就要求模具本身就有真空管路!</P>

mrfeng

缩小铺料面积。